    Characterization of boron doped Cobalt/Zinc acetate composite fibers
    (2009) Uslu, İbrahim; Gökmeşe, Faruk; Atakol, Orhan; Aksu, Mehmet Levent
    PVA/cobalt acetate/zinc acetate doped with boron composite fibers were prepared by electrospinning technique. Electrospinning was performed by putting solutions at different applied voltage in a range from 13 to 18 kV. The fibers were measured and characterized by viscometer, conductiometer (with fourpoint probe), Fourier transformed infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), and differential scanning calorimetry (DSC). The viscosity of the Boron doped solution was higher and favoring the formation of thinner and uniform nanofibers. DSC analysis shows that when boron is added to the polymer it increases the crosslinking and amorphous structure of PVA/ cobalt and zinc acetate composite polymer is increased.
  • Küçük Resim Yok
    Öğe
    Preparation and characterization of PVA/Boron polymer produced by an electrospinning technique
    (EUROPEAN POLYMER FEDERATION, 2007) Uslu, İbrahim; Daştan, H.; Altaş, Ayşenur; Yaylı, Ahmet; Atakol, Orhan; Aksu, Mehmet Levent
    In this study, poly(vinyl alcohol) were cross-linked with boron in varying concentrations and blend fibers were obtained with diameters ranging from 0.3 mu to 4.0 mu m with the use of electrospinning process. The resulting product was characterized by SEM, DSC, and FT-IR techniques. There is no beading tendency in either boron doped or undoped fibers. When the amount of boric acid in PVA solutions was increased the conductivity of the polymer decreased. The data indicated the existence of boron oxide in the polymeric structure and the formation of B-O-C bond. SEM micrographs reveal that higher viscosity favors the formation of thicker fibers. Boron addition seems to disturb the easy detachment of the fibers from the tip of the Taylor Cone.
  • Küçük Resim
    Öğe
    Preparation of PVA/Chitosan Doped With Boron Composite Fibers and Their Characterization
    (2008) Uslu, İbrahim; Çelikkan, Hüseyin; Atakol, Orhan; Aksu, Mehmet Levent
    In this study, chitosan and poly(vinyl alcohol) were cross-linked with boron in varying concentrations and chitosan and poly(vinyl alcohol) blend fibers were obtained with electrospinning process. Viscosity and electrical conductivity results revealed that the increase in chitosan and boron content increased the viscosity of the solution and but decreased the electrical conductivity of the fibers. The peaks obtained with FT-IR analyses were in good agreement with literature. SEM micrographs also showed that wavy and curly fibers with relatively small diameters were obtained as the chitosan and boron concentrations were increased. Thermogravimetric data revealed that the formation of a more stable polymer structure as a result of the cross linking with boron.
  • Küçük Resim
    Öğe
    Şehir İçme Suyu Arıtma Tesislerinde Çamur Atıklarının Değerlendirme Yollarının Araştırılması
    (Selçuk Üniversitesi Fen-Edebiyat Fakültesi, 2005) Atakol, Orhan; Arslan, Gülşin
    Bu çalışmada, Ankara İvedik İçme Suyu Arıtma tesislerinde suyun arıtılma işlemi sonucunda atık olarak ele geçen jelimsi çamurun kimyasal yapısı araştırılmıştır. Kimyasal analizler hem klasik hem de Atomik Absorpsiyon yöntemleri kullanılarak yapılmıştır. Tarımsal açıdan mahsurunun olup olmadığı sera deneyleri yapılarak araştırılmıştır. Araştırma sonucunda atık çamurun ana bileşeni Al(OH)3 olup zaman içinde suyunu kaybederek okside dönüşmekte ve taşlaşmaktadır. Saksı deneylerine bakılırsa atık çamur içinde çimlenme olabilmekte ancak kontrol grupları ile karşılaştırıldığında çimlenme süresinin uzadığı kök ve yaprak boyunun kısaldığı görülmektedir. Bu atık çamurun çevreye kirletici etkisi olmadığı gibi pek bitki dostu da değildir. Ayrıca Al(OH)3 jelinin çökmesini hızlandırmak amacıyla ilave edilen polielektrolitin çimlenmeye etkisi olmadığı gibi yararlı olacağı düşüncesi ortaya çıkmıştır. Su arıtma tesislerinde en yüklü masraf Al2(SO4)3 için harcandığından dolayı, yüksek %’de Al bulunduran bu atık çamurdan yeniden Al2(SO4)3 eldesi araştırılmalıdır